Dekalin DEKAsyl MS 2 MS- Polymer Adhesive Sealant 290 ml (Grey)

Base material: MS Polymer
Curing / Sealing: Moisture

Specific weight: approximately 1.4 kg/litre
Skin formation time (20°C/50% rel. LF): approx. 10 minutes

Opening time (20°C/50% rel. LF): < 15 minutes
Hardening after 24 hours (20°C/50% rel. LF): approx. 3 mm

Shore A hardness (DIN 53505): approx. 55
Volume change (DIN 52451): < 3%.

Adhesion strength (MC100 Physical Rheometer): about 300 Pa
(Measure the maximum amount of adhesive that can be applied per m² without sagging)

Tensile stress (100%) (DIN 53504/ISO 37): approx. 1.7 Mpa
Tensile stress at break (DIN 53504/ISO 37): approx. 2.6 MPa

Elongation at break (DIN 53504/ISO 27): approx. 250%.
Shear stress (DIN 53283/ASTM D1002): approx. 2.5 MPa

Tear strength (DIN 53515/ISO 34): approx. 16 N/mm

Solvent content: 0%.
Isocyanate content: 0%.

Temperature resistance: -40°C to +120°C
Application temperature: from +5°C to +35°C

Resistance to UV rays and atmospheric agents: excellent

DEKAsyl MS-2 is the ideal compromise between an adhesive and a sealant for creating elastic connections between components that also require high adhesive strength.
DEKAsyl MS-2 glues and seals in a single treatment, does not weaken the material used and leaves no traces of connecting elements (screws or similar).
Repainting of the MS-2 adhesive sealant is possible after the film has formed.

The fields of application and use are multiple and can be expanded according to needs.

Color: Grey
Content: 290 ml
Packaging: Cartridge

Areas of application:

- Aluminum
- Polisester
- GFK (glass fiber reinforced plastic)
- PMMA (polymethyl methacrylate abb. PMMA or also acrylic glass) is a transparent thermoplastic
- Compensation for structural tolerances
- Glass
- Skylights - and windows
- Wheel fairings
- and much more